Apparatus for processing of finely divided particulate materials

ABSTRACT

A mass of finely divided material is confined in a chamber. Two rollers are arranged for rotation in the chamber in axial parallelism with one another and define with each other a narrow longitudinally extending gap. At least one of the rollers has a circumferential wall composed of gas-permeable porous material. This one roller is hollow and arranged to communicate with a source of underpressure so that, as the roller rotates, the particulate material is attracted onto its outer surface forming a layer thereon which is subjected to substantial compaction when it passes through the gap between the two rollers. The rollers rotate in opposite direction. The compacted material is removed from the outer surface of the roller or rollers and subdivided into portions of desired size. A method of processing the particulate material, and a roller for use in the apparatus are also disclosed.

[ June 12, 1973 United States Patent [1 1 Reinhardt et al.

Perry 162/333 X l8/DIG. 62 18/9 3,329,198 7/1967 Manning....... 2,662,246 12/1953 Klugh et al. Primary Examiner-H. A. Kilby, Jr. Att0rneyMichael S. Striker [73] Assignee: Deutsche Gold-Und Silber-Scheideanstalt Vormals ABSTRACT Roessler, Frankfurt am Main, Germany Filed Nov 6 1969 A mass of finely divided material is confined in a cham- Appl. No.: 874,654

ber. Two rollers are arranged for rotation in the chamber in axial parallelism with one another and define with each other a narrow longitudinally extending gap.

[ Foreign Application priority Data At least one of the rollers has a circumferential wall composed of gas-permeable porous material. This one NOV. 8, P roller is hollow and arranged to communicate a source of underpressure so that, as the roller rotates, [52] CL 425/85 162/297 125/224, the particulate material is attracted onto its outer sur- 425/363, 425/455 [51] Int.

face forming a layer thereon which is subjected to substantial compaction when it passes through the gap between the two rollers. The rollers rotate in opposite direction. The compacted material is removed from the outer surface of the roller or rollers and subdivided into portions of desired size. A method of processing the particulate material, and a roller for use in the apparatus are also disclosed.

18/15 F, 19 F, DIG. 62; 162/297, 323, 324, 325, 326, 327, 328, 329, 330, 331, 332, 333

[58] Field of Search 18/9 [56] References Cited UNITED STATES PATENTS 2,689,653 9/1954 Ohlstrom APPARATUS FOR PROCESSING OF FINELY DIVIDED PARTICULATE MATERIALS BACKGROUND OF THE INVENTION The present invention relates generally to the processing of finely divided particulate materials, and more specifically to the processing of such materials which requires pre-condensing and subsequent compacting of such materials into desired shapes. The invention relates to a method for effecting such processing, to an apparatus for carrying out the method and to a roller for use in the apparatus.

In many instances the processing of finely divided particulate material, such as pulverulent or finecrystalline and organic materials, frequently depends upon the possibility of increasing the volumetric weight of such materials without destroying or adversely influencing their specific characteristics which depend upon the fine division of such materials. This is particularly true of highly dispersed surface-active filler materials, such as silicon oxide, carbon black, aluminum oxide, aluminum silicates and calcium silicates, all materials which are used in very large quantities in various industries.

The problems involved in the processing of these materials are not insignificant. On the one hand, in their finely divided state they require relatively large amounts of space for storage and transportation, an obvious disadvantage. Furthermore, they tend to dust and to undergo uncontrollable caking, both of which are of course characteristics of their finely divided state which are'clearly detrimental to economic handling and' proper processing.

Industry has attempted to find solutions to these problems, and particularly to impart to such finely divided materials a state in which their specific characteristics-such as the ability to disperse in the case of finely divided active filler materials-are fully retained while the space required for storage and transportation is substantially reduced, and dusting during filling, me-

' v tering and processing is largely eliminated. It has been moved, because otherwise it is not possible to obtain agglomerates with sufficient adhesion under mechanical pressure. It has been found, for instance, that it is impossible to obtain the desired compaction and adhesion simply by passing such materials between two metal rollerswhich subject them to mechanical compression. Therefore, gas removal and pre-condensing has been resorted to, utilizing in known continuously operating apparatus of the typein question pressuretype conveyor screws, rollers or pairs of rollers provided with radial projections or provided on the surface of at least one roller with profiling. However, it has been found that the degassing or outgassing effect and compaction obtainable with such apparatus, which for the actual compaction utilizes a pair of pressure rollers, is inadequate compared to the complexity and expense of the apparatus involved.

A further approach which has been tried is to deposit the material to be compacted onto hollow rollers, socalled filter rollers, whose circumferential wall is gaspermeable and whose interior is subjected to underpressure. The gas is thereby withdrawn from the deposited material and the material is supplied by the filter rollers to the compacting gap between a pair of pressure rollers. Various modifications have been proposed for this basic approach but in each case the gap between the pressure rollers-in which the material is subjected to compactionis fixed. This approach is limited in its applicability because it permits only the production of compressed blanks, as the compacted bodies made from the compacted finely divided particulate materials will hereafter be called for the sake of convenience, without specific form and only within a rather broad range of grain sizes. A further disadvantage is that the compacted blanks obtained in this manner have a widely varying breaking resistance, a fact which is of particular disadvantage if the compacted blanks are of filler material which is intended for certain applications, for instance for use in rubber mixtures, because with the mixing procedure used in the production of rubber mixtures the compacted blankS can be broken down only partially to the original grain size. The result of this is an inadequate dispersal of the filler material and the resulting typical formation of pockets and cavities in the vulcanized goods.

In addition certain materials, for instance light reinforcing filler materials such as SiO can be compacted only to a bulk density of approximately 250 g/l in the apparatus known from the prior art and utilizing the socalled filter rollers, because the low mechanical strength of the fabrics used for the circumferential walls of the filter rollers makes it impossible to utilize higher compacting pressures. This is quite aside from the fact that even at these lowered operating pressures the fabrics must be very frequently replaced.

SUMMARY OF THE INVENTION It is, accordingly, an object of the present invention to overcome the aforementioned disadvantages.

A more particular object of the invention is to provide a method of processing finely divided particulate materials which is not subject to the disadvantages outlined before. I

A concomitant object of the invention is to provide such a method which enables continuous operation and the production of compacted blanks of specific desired shape and size with a defined narrow range of breaking resistance and increased bulk weight.

An additional object of the invention is to provide an apparatus for carrying out the method.

Still a further object of the invention is to provide a roller construction for use in such apparatus.

In pursuance of the above objects, and others which will become apparent hereafter, one feature of the invention resides in the novel method which, briefly stated, comprises confining a mass of finely divided material adjacent the gas-permeable circumferential wall of a rotatable roller having a hollow interior. The roller is thereupon rotated and subjected in its interior to underpressure so as to attract the material by suction to the exterior of the circumferential wall of the roller for forming a continuous layer of the material thereon. Another roller is rotated in axial parallelism with the rotatable roller and with such a spacing from the exterior of the same as to define with the latter a gap wherein the layer is subjected to compacting.

The roller having the gas-permeable circumferential wall, hereafter for the sake of convenience called the filter roller, may rotate partially or completely in the material to be compacted, and the same is true of the other roller. The thickness of the layer may be maintained constant by removing excess attracted material from the layer before increments of the layer enter into the gap between the two rollers. In accordance with the invention, one of the two rollers is biassed towards the other with a biassing force which is preferably maintained at constant level. The other roller may also be a filter roller or it may be a roller having a known gasimpermeable circumferential wall. In any case, the layer is compacted on passage of the gap between the two rollers so as to be reduced by at least one half of its original volume and is deformedby profiling provided on the circumferential wall of at least one of the rollers-into compacted blanks of desired shape and configuration and defined range of breaking strength.

It is desired and advantageous according to the present invention that the dwell time of the material of the layer, that is of the material of which each successive increment of the layer is composed which enters into the gap between the two rollers, be below approximately 5 seconds, a time value which of course depends upon the roller circumference and the speed of rotation of the rollers.

In accordance with the invention it is not necessary that two rollers be provided having a gas-permeable or porous circumferential wall, or that even two rollers of the same type be rotated oppositely one another. However, for granulating purposes it is desirable and preferable that one of the two rollers has a profiled surface of circumferential wall. Depending upon the profiling, compacted blanks of certain configuration are obtained, for instance granules, little rods, tablets and the like. For instance, if the profile is half-moon shaped, then the compacted blanks will be similarly configurated. These compacted blanks may then be reduced to the desired dimensions in a cutting device of known construction, for instance in a so-called rotary disc breaker. Because of the profiling on at least one of the rollers, at least two dimensions of the resulting product are already established before the cutting device acts upon the compacted blanks.

The novel features which are considered as characteristic for the invention are set forth in particular in the appended claims. The invention itself, however, both as to its construction and its method of operation, together with additional objects and advantages thereof, will be best understood from the following description of specific embodiments when read in connection with the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWING FIG. 1 is a partially sectioned diagrammatic perspective view of an apparatus according to the present invention; and

FIG. 2 is a partly sectioned somewhat diagrammatic perspective view illustrating one embodiment of a roller according to the present invention for use in the apparatus of FIG. 1.

DESCRIPTION OF THE PREFERRED EMBODIMENTS As shown in FIG. 1, the apparatus comprises a housing 1 having two transversely spaced walls la. Mounted in the housing 1 is a filter roller 2, for instance of the type which will be discussed more specifically with reference to FIG. 2. The roller 2 is hollow, and arranged for rotation in axial parallelism with the roller 2 is the roller 3 rotating in the direction opposite to the roller 2, as indicated by the arrows respectively associated with the two rollers. The circumferential wall of the roller 3 is not gas-permeable, and the roller 3 is therefore not designated as a filter roller as is the case with the roller 2. Instead, the circumferential wall of the roller 3 is provided on its exterior with a half-moon shaped longitudinal profile 4, shown in cross-section.

According to the invention the dimensions of the housing 1 are so selected that the spacing between the filter roller 2 and the housing walls 1 in direction normal to the longitudinal axis of the filter roller 2 is substantially greater than the gap between the rollers 2 and The shaft 15 about which the filter roller 2 rotates is hollow and a suitable source of underpressure may be connected with it in order to obtain underpressure in the interior of the filter roller 2.

A measuring transducer 13a and a PI regulator 13b which is coupled with an indicator device 13c, permit regulation of the value of underpressure applied to the interior of the filter roller 2, via a valve l3e.

Slide bearings 9 journal the shaft 15 of the filter roller 2, permitting movement of the latter in the direction towards and away from the roller 3. Biassing devices 7, which here are illustrated as being of hydraulic type but which could be mechanically or pneumatically operated, act upon the bearings 9 and bear upon a support structure 8 which is located exteriorly of the wall In of the hOusing 1. A hydraulic pump 12a provides the necessary biassing force whose value is registered on the indicators 12b. If a pressure increase takes place in the system as a result of changes in the size of the gap between the rollers 2 and 3, caused by increased thickness of the layer of material as it enters the gap or by other factors, the increased pressure can yield and fluid escapes into the two reservoir bulbs which are provided. Two pressure relief valves 12d are provided intermediate the reservoirs 12c and the biassing devices 7 in order to assure that the applied isodynamic pressure is so reduced only after it reaches a certain level. If the manually operated hydraulic pump 12a is replaced with an electrically operated pump, then a maximum-minimum or limit switch He must be provided for effectinG automatic regulation of the desired biassing pressure.

A hopper 14 communicates with the interior space 5 in the housing 1 for introducing into the space 5 the finely divided particulate material which is to be compacted. When underpressure is applied to the interior of the rotating filter roller 2, the particulate material is attracted to the outer surface of the circumferential wall of the filter roller 2 to form a layer thereon which then passes into and through the gap between the rollers 2 and 3. It is desirable to provide an adjustable and shiftable doctor blade 10 above the filter roller 2 for removing material from the attracted layer in excess of a predetermined thickness, in order to provide for as much thickness equalization of the attracted layer as possible before the same enters into the gap between the rollers 2 and 3. The compacted material, having the configuration imparted to it by the profiling 4, falls out of the gap between the rollers 2 and 3, and downstream of the gap it is cut to desired lengths by the cutting device provided, here illustrated as a known disc breaker or rotary disc breaker 11.

FIG. 2 illustrates a specific embodiment of a filter roller for use in the apparatus according to the present invention. Reference numeral identifies the hollow shaft a portion of which is provided with bores 15a. There are provided two side walls or end walls 17 of disc-shape which are gas-tight with the hollow shaft 15 at the opposite axial sides of the region in which the bores 15a are provided. There is further provided a circumferential wall 16 of cylindrical configuration which is provided with a plurality of small bores or other apertures 16a. The wall 16 is fluid-tightly connected with the end walls 17, for instance by welding, and in the same manner the walls 17 may be connected with the shaft 15. 7

Provided on the exterior of the cylindrical circumferential wall, which may also be called the inner circumferential wall 16, is an outer circumferential wall composed of a plurality of plates 18 of sintered material, for instance metallic sintered material, synthetic plastic sintered material or ceramic sintered material. These plates 18 abut one another and, insofar as they are composed of weldable material, are welded to the inner circumferential wall 16 as well as to one another where they abut. However, screw means may also be provided for securing the blades 18 to the inner circumferential wall 16. The inner circumferential wall 16 is provided with interior radial reinforcing ribs 19 for increasing the strength and stability of the roller, but helically convoluted ribs or axially extending ribs may also be pr0- vided, or any combination of the three. Reference numeral 20 identifies the inlet opening of the hollow shaft 15 at which underpressure may be applied.

It has been found that the production of compacted blanks with defined range of break resistance is facilitated by maintaining a constant level of biassing pressure of the rollers 2 and 3 towards one another. In order to obtain only small fluctuations of this range it is advisable to mount one or both of the rollers in the manner shown in FIG. 1, that is in such a manner that the gap width can change automatically in dependence upon the thickness of the layer carried by the filter roller, or the compaction of the material in the gap, or

other factors, thereby assuring that the compacting and compression is always effected with identical mechanical pressure. Furthermore, such a construction of course reduces the possibility of breakdown of the apparatus.

The level of this isodynamic pressure depends in each individual case upon the particulate material to be compacted, its moisture content and the degree of compacting which is desired. In the case of white filter materials, such as silicium dioxide, the moisture content is for instance desirably not below 1 percent.

The optimum break resistance of the compacted blanks made from a given particulate material depends upon the intended use and can readily be determined by empirical means. For instance, it has been found that SiO granulates produced in accordance with the present invention have adequate transport stability and maximum dispersion characteristics in-a test rubber mixture if a break resistance to pressure between 100 and 500 pond (p) is obtained in the compacted blanks, measured with the hardness tester'according to German Auslegeschrift l 374 254. The term breaking I dwell time in the gap 6' pressure is intended to mean the pressure in ponds which is necessary to abruptly destroy a granulate of 2 3 mm grain size.

The dispersion characteristics of SiO compacted blanks made in accordance with the present invention may for instance be determined in a test mixture colored with ferrous oxide red. In this case, the test mixture is introduced into a mixer of the internal type and under identical circumstances one bath of test mixture has admixed therewith silicium dioxide granulate made according to the present invention whereas another batch has admixed therewith for comparison purposes a silicium dioxide powder. After the two batches are mixed a simple optical comparison indicates if and to what extent dispersion has been improved. It has been found, surprisingly, that if the breaking pressure of the compacted silicium dioxide blanks is set to between 200 and 250 ponds, the dispersion in the test mixture is substantially better than in the test mixture to which the silicium dioxide powder was added.

For instance, if the original finely divided particulate material is a SiO, powder with primary particle sizes smaller than 50 p. and with a bulk weight of approximately g/l, then a SiO granulate according to the present invention and having breaking pressure values between 200 and 250 ponds may be produced under approximately the following circumstances:

roller pressure approximately l-6 mm, up to approximately 4 mm play in direction normal to the roller axes approximately 0.0l-0.l sec.

underpressure applied approximately 0.3-0.95 kg/cm to filter roller gas permeability of the filter roller surface approximately 6 m lcm X 1 ter roller into the roller gap, that is prior to the compacting which takes place in the roller gap itself, a precompacting or precompressing to a bulk weight of approximately 250 g/l is obtained in this case.

If for instance one of the rollers has a half-moon shaped longitudinal profile in its outer circumferential surface with dimensions of 6 X 2 mm, then a finished granulate with approximately the following screen analysis is obtained by breaking the rod-shaped Si0 compacted blanks falling out of the gap between the rollers in a conventional rotary disc breaker and subjecting them subsequently to screen removal of the fines smaller than 0.5 mm;

Particle Size mm 34 30 2-3 35 1-2 25 0.5-l l0 Enlarged photographs of the individual sieve or screen fractions of the finished granulate show that the form obtained for the compacted blanks during compaction in the gap between the rollers is readily visible in case of the fraction 3 5 mm, and that it is still readily identifiable in case of the fraction 2 3 mm.

This means that the identifiably shaped granulate quantity amounts to 65 percent, that is the total of the fractions 3 mm and 2 3 mm.

It will be appreciated that unlike the embodiment illustrated in FIG. 1, it is possible to mount the filter roller 2 for rotation but not for shifting movement, and to mount the roller 3 for such shifting movement. However, the embodiment illustrated in FIG. 1 is preferred.

It is advantageous in accordance with the present invention that the pores of the material of which the outer circumferential wall of the filter roller is composed be so dimensioned that at a predetermined operational load of the suction device an underpressure of constant value in the interior of the filter roller, irrespective of whether the filter roller is partly or completely immersed in the material to be compacted.

If, as illustrated in the embodiment of FIG. 1, a rotary disc breaker is arranged below the gap between the rollers 2 and 3, then it is advantageous that the cutting edges of the rotary discs of the breaker extend in planes transversely to the elongation of the gap. This is particularly advantageous if the apparatus according to the present invention produces compacted blanks in profiling which extends longitudinally of the rollers.

The material for the porous outer circumferential wall of the filter roller is a suitable sinter material, such as sinter metal, sinter synthetic plastic or sintered ceramic. It is of course not necessary that the outer circumferential wall consist of the plate-shaped portions illustrated in FIG. 2, but this enhances the stability.

It is advantageous, but not absolutely necessary, that the spacing of the filter roller from the bottom wall of the housing I be at least equal to half the roller diameter, and that the lateral spacing between the sinter roller and the housing wall be equal to at least one roller diameter. The doctor blade mentioned before may be adjustably mounted so as to movable towards and away from the circumferential wall of the filter roller, and it may also be so mounted that its angle with respect to the circumferential wall can be adjusted.

The pores of the porous material of the outer circumferential wall of the filter roller may havea diameter of approximately 0 200 IL, preferably between 0 35 u. The thickness of the outer circumferential wall should be at least approximately 1 mm. At underpressures of 0.01 1.0 kg/cm the gas permeability of the outer circumferential wall of the filter roller may be in the regionbetween approximately 0.1 and 7 m /cm X h.

The roller according to the present invention, for utilization in the apparatus according to the present invention, has certain very definite advantages over the rollers used in known apparatus, namely a long life irrespective of whether it is rotated at low or high rotational speeds, resistance to much higher pressure than are possible with the known constructions, and retention of its shape, that is resistance to being deformed so it is out-of-round in cross-section.

The following examples will further aid in an understanding of the invention.

EXAMPLE 1 In an apparatus according to FIGS. 1 and 2 compacted blanks of highly dispersed surface active silicium dioxide were produced. The starting material, obtained by precipitation from an aqueous silicate solution, had the following characteristics:

Dry loss (105) approximately 6% 8 Specific weight 1.9-2.0 Bulk weight 80-1 10 g/l Vibratory weight 160-200 g/l BET-surface 240 m Primary particle 16 p diameter The apparatus utilized an isodynamically biassed filter roller and a non-adjusted rotatable rotatable nongas permeable counter roller having half-moon shaped longitudinal profiling. Both rollers were 300 mm long and had a diameter of 100 mm. The outer circumferential wall of the filter roller was 5 mm thick and consisted of sinter metal Siperm R" (Remanit) having a maximum pore width of 35 t. The profile of the counter roller had the dimensions 6 X 2 mm. Arranged below the gap between these rollers was a rotary disc type breaker with a spacing between the disc of 3 mm.

Prior to operation of the device the housing was filled via the hopper to approximately two-thirds with the pulverulent material to be compacted, a roller pressure of 0.35 t/cm was set and an underpressure of 0.6 kg/cm was applied to the filter roller. The doctor blade arranged above the filter roller was set at a distance of 15 mm from the circumferential wall of the filter roller. Thereupon, both rollers and the disc type breaker were simultaneously started. The rotation of the rollers was so regulated that the medium dwell time of the material to be compacted in the gap between the rollers was approximately 0.15 sec. The width of the gap was approximately 1 mm. The movements of the filter roller in direction normal to the axes of the two rollers, which oc curred during the compacting operation, were in the range of between 1 3 mm. The bulk weight of the precompacted particulate material forming a layer on the filter roller prior to entering into the gap was 255 gl. The output obtained was approximately 260 kg/h granulate having a bulk weight of 330 g/l. The breaking pressure of the compacted blanks was between 200 and 250 pond.

After screening and classification to particle sizes between 0.5 5 mm, only a fine smaller than 0.5 mm amounting to 15 percent was left.

Sieve analysis on a laboratory sieve or screen of commercially available type showed the following values in the final product:

Particle Size O. 0. l. 1. l. 3.

The granulate portion having an identifiable shape (fractions 5, 3 5 mm and 2 3 mm) corresponded to 62.6% of the total.

The dispersion ability of the granulates was tested in a red colored test rubber mixture free of vulcanizing additives. A 'Brabender-Plastograph was used as disper- SIOII apparatus.

TEST MIXTURE AND DISPERSION CONDITIONS Polysurbutyl 301 (Polysar Co., Belgium). type non-staining; isopren content of [.6 Mo|-%: Mooney-viscosity ML 8:85 (at 212 F) "Consisting of 100 parts polysarbutyl 30l and 50 parts iron oxide red *Softener (Tributoxyethylphosphat) Manufacturer: Food Machinery and Chemicals Corporation, New York.

' The mixtures thus obtained were subsequently passed at 95 C and at a gap setting of 1 mm three times through a laboratory two-roller frame and then rolled EXAMPLE 2 (COMPARISON TEST) The starting SiO material used in the Example 1 for producing granulates was pressed with a known apparatus of comparable dimensions. Precompression took place via a vertically operated screw and compacting took place in the gap between two oppositely rotating metal rollers whose circumferential walls were provided with wave-shaped serrations. In order to be able to at all obtain a granulate break resistance on the order of 200 pond it was necessary to pass the SiO repeatedly through the gap between the rollers. The production output was only 50 kg/h. The granulate dispersion in the test mixture produced in accordance with Example 1 was significantly poorer than that of the test mixture utilizing the purverulent starting material. It was a particular'disadvantage that the fines 0.5 mm obtained on classification in the range between 0.5 5 mm was 50 percent after the first compacting,

and could be reduced to approximately percent only by repeated compacting.

It will be understood that each of the elements described above, or two or more together, may also find a useful application in an apparatus for processing finely divided particulate materials differing from the types described above.

While the invention has been illustrated and described as embodied in other types of constructions, it

- said housing at least partially immersed in said mass and for rotation relative thereto; a second roller mounted in said housing for rotation in axial parallelism with said first roller spaced from and defining with the same an axially extending gap of a predetermined minimum width exceeding zero, one of said rollers being movable away from the otherroller transversely of said gap so that the latter may increase in width; biasing means for yieldably biasing said one roller to- 'wards the other transversely of said gap with a biasing force of constant value under all operating conditions; and suction means communicating with the interior of said first roller for exerting through said gas-permeable circumferential wall thereof a suction effect on said material to thereby effect deposition of said material on said wall in form of a layer for subsequent compacting in response to passage of increments of said layer through said gap.

2. Apparatus as defined in claim 1, wherein said circumferential wall is porous.

3. Apparatus as defined in claim 1, wherein said circumferential wall consists at least in part of sintered metallic powder.

4. Apparatus as defined in claim 1, said housing having a pair of spaced walls located at opposite sides of and each extending in at least substantial axial parallelism with said rollers; and wherein the smallest distance between said circumferential wall of at least said first roller and the associated wall is at least three times greater than the width of said gap.

5. Apparatus as defined in claim 4; said second roller having a non-permeable second circumferentialwall.

6. Apparatus as defined in claim 4, each of said rollers having an outer circumferential surface, and wherein at least one of said surfaces comprises profilmg.

7. Apparatus as defined in claim 1, said chamberhaving a bottom wall below said rollers, and said first roller having a predetermined diameter; and wherein the distance between said first roller and said bottom wall is at least equal to one half of said diameter.

8. Apparatus as defined in claim 4, said first roller having a predetermined diameter, and said smallest distance being at least equal to said predetermined diameter.

9. Apparatus as defined in claim 1; further comprising a doctor blade extending along the exterior of said circumferential wall in axial parallelism with said first roller; and mounting means mounting said doctor blade adjustably for movement towards and away from said prising journalling means mounting said first roller rotatably and for adjusting movement toward and away from said second roller.

13. Apparatus as defined in claim 1, said biasing means comprising a fluid-operated biasing device.

14. Apparatus as defined in claim 12, said second roller having a longitudinally profiled outer surface; said first roller and comprising journalling means journalling said first roller rotatably and for movement towards and away from said second roller; and said biasing device biasing said first roller toward said second roller.

15. Apparatus as defined in claim 2, said circumferential wall being provided with pores having a combined cross-sectional area so selected that said suction means maintains an at least substantially constant level of suction in said first roller irrespective of the extent to which the latter is immersed in said mass. 

1. Apparatus for processing finely divided particulate material, comprising a housing defining a chamber for accommodating a mass of finely divided solid particulate material; a hollow first roller having a gas-permeable circumferential wall and being mounted in said housing at least partially immersed in said mass and for rotation relative thereto; a second roller mounted in said housing for rotation in axial parallelism with said first roller spaced from and defining with the same an axially extending gap of a predetermined minimum width exceeding zero, one of said rollers being movable away from the other roller transversely of said gap so that the latter may increase in width; biasing means for yieldably biasing said one roller towards the other transversely of said gap with a biasing force of constant value under all operating conditions; and suction means communicating with the interior of said first roller for exerting through said gas-permeable circumferential wall thereof a suction effect on said material to thereby effect deposition of said material on said wall in form of a layer for subsequent compacting in response to passage of increments of said layer through said gap.
 2. Apparatus as defined in claim 1, wherein said circumferential wall is porous.
 3. Apparatus as defined in claim 1, wherein said circumferential wall consists at least in part of sintered metallic powder.
 4. Apparatus as defined in claim 1, said housing having a pair of spaced walls located at opposite sides of and each extending in at least substantial axial parallelism with said rollers; and wherein the smallest distance between said circumferential wall of at least said first roller and the associated wall is at least three times greater than the width of said gap.
 5. Apparatus as defined in claim 4; said second roller having a non-permeable second circumferential wall.
 6. Apparatus as defined in claim 4, each of said rollers having an outer circumferential surface, and wherein at least one of said surfaces comprises profiling.
 7. Apparatus as defined in claim 1, said chamber having a bottom wall below said rollers, and said first roller having a predetermined diameter; and wherein the distance between said first roller and said bottom wall is at least equal to one half of said diameter.
 8. Apparatus as defined in claim 4, said first roller having a predetermined diameter, and said smallest distance being at least equal to said predetermined diameter.
 9. Apparatus as defined in claim 1; further comprising a doctor blade extending along the exterior of said circumferential wall in axial parallelism with said first roller; and mounting means mounting said doctor blade adjustably for movement towards and away from said circumferential wall and for adjustment to a plurality of angular positions with reference to said circumferential wall.
 10. Apparatus as defined in claim 1, wherein at least one of said rollers is provided with external profiles.
 11. Apparatus as defined in claim 10, wherein said external profiles extend axially of said one roller.
 12. Apparatus as defined in claim 5, and further comprising journalling means mounting said first roller rotatably and for adjusting movement toward and away from said second roller.
 13. Apparatus as defined in claim 1, said biasing means comprising a fluid-operated biasing device.
 14. Apparatus as defined in claim 12, said second roller having a longitudinally profiled outer surface; said first roller and comprising journalling means joUrnalling said first roller rotatably and for movement towards and away from said second roller; and said biasing device biasing said first roller toward said second roller.
 15. Apparatus as defined in claim 2, said circumferential wall being provided with pores having a combined cross-sectional area so selected that said suction means maintains an at least substantially constant level of suction in said first roller irrespective of the extent to which the latter is immersed in said mass. 